Fast Cycle 211 Sb S S2 S3 - Taiwanprice: contact company for price
SB- 211 S- 211 S2- 211 S3- 211
BEAD SIZE 1.2- 1.8mm 0.9- 1.3mm 0.7- 1.0mm 0.5- 0.8mm
DENSITY 14~18g/ cm³ 15~20g/ cm³ 16~25g/ cm³ 17~30g/ cm³
APPLICATION Block, Plate Large package Medium Package Package- thin item Package- small item
HUMIDITY ↓ 1%
SPECIFIC GRAVITY APPROX. 1.03
PENTANE LEVEL 6.5~ 7.5%
POLYSTYRENE ↑ 92.5%
The steam must be saturated at the temperature of 95~105°C. To reach the density we demand with a continuous or batch type performer, sometimes pre- foaming twice is recommended, when we want the density below 12 kg/ m³
Generally, 6- 24 hours is recommended, depends on the density. Between the two steps performing, the conditioning time for 4~8 hours is suggested.
The machine should be fed with saturated steam with the maximal pressure of 1.3~1.5 bar ( about 105~110ºC) . The steaming time depends on the equipment used as well as the required size and strength of the final product. Therefore, all the machines must be adjusted individually. In order to reduce the cycling time and to increase the strength of the product, the vacuuming of the equipment is recommended.
EPS should be stored indoor, and in a cool and good ventilated place. The storage temperature shall be maintained below 20ºC. The lower, the better. * Once bag is opened, shall be used as soon as possible to maintain freshness, ' FIRST IN FIRST OUT ' .
- Posted By: B2BMIT
- Phone: 886422362908
- Address: Rm. 5, 11F., No.238, Jinhua N. Rd., North Dist.,Ta, Taichung, Taiwan
- Website: http://www.b2bmit.com
Published date: April 24, 2014 -
- Business Description: B2BMit is a trade platform of providing manufacturers Made In Taiwan ,
consisting various classifications and more than 50,000 suppliers.
Self Extinguishing Flame Retardent Ul94Plastic - Raw Materials - B2BMIT - Taiwan - April 24, 2014 - contact company for price
SPECIFICATION FM FS BEAD SIZE 0.9- 1.8mm 0.5- 1.0mm DENSITY 15~25g/ cm³ 16~30g/ cm³ APPLICATION Construction / Block Construction / Package HUMIDITY ↓ 2% SPECIFIC GRAVITY APPROX. 1.03 PENTANE LEVEL 5.5~6.5% POLYSTYRENE ↑ 92.5% Preforming:...
Modified Plastic Raw Material Reinforced Nylon Pellets Pa6 Pa66Plastic - Raw Materials - Changzhou Nanyang Plastic Tecnology Co.,Ltd. - China - April 16, 2014 - contact company for price
This is manufacture form china producing Modified Engineering Plastic pellets. PA6 GF15% - - GF40% PA66 GF15% - - GF40% Virgin grade . White and natural color or as customers’ request. Vacuum packaging with Aluminum film, 25kg/ bag, We also can provi...
Nylon Chips Polyamide6 And Polyamide66 With Glass Fiber Filled InPlastic - Raw Materials - Changzhou Nanyang Plastic Tecnology Co.,Ltd. - China - April 16, 2014 - contact company for price
Place of Origin China ( Mainland) Brand Name Xiongfeng Appearance pellets & granules OEM Yes Grade Virgin off grade & modified polyamide66 resin pa66 gf30 pellets for injection molding polyamide66 resin pellets for injection molding, pa66 gf30 WE ARE...
Safe Trade Tips
- Ask for business references and check them
- Verify their business via their local Chamber of Commerce