Asme Sa 517 517m High Tensile Alloy Steel Plates For Pressure Vessels - China

ASME SA-517/SA-517M high tensile alloy steel plates for pressure vessels

Specification :

SA517 in the standard SA-517/SA-517M is a kind of high tensile alloy steel plates material used to fabric high temperature pressure vessels.

SA517 have six grades or levels.

They are : grade A, grade B, grade E, grade F, grade J , grade P.

SA517 need to be done the (Quenching + Tempering ) heat-treatment to meet the property requirement in the standard ASTM SA-517/SA-517M.

Standard: ASME SA-517/SA-517M

Steel Grade : SA517 GR A, SA517 GR B, SA517 GR E, SA517 GR F, SA517 GR J, SA517 GR P steel.

Dimension range : 3mm -260mm x 1000mm-4000mm x 1000mm-18000mm

MOQ: 1 PC

Delivery time : 10-40 days (Production)

Stock : Unvailable

MTC: Available

Payment Term : T/T or L/C At sight .

ASTM SA-517/SA-517M SA517 steel chemical composition :

%

Composition Grade A Grade B Grade E Grade F Grade J Grade P

C Heat analyse 0.12~0.21 0.10~0.20

Product analyse 0.10~0.22 0.08~0.22

Mn Heat analyse 0.80~1.10 0.70~1.00 0.40~0.70 0.60~1.00

Product analyse 0.74~1.20 0.64~1.10 0.35~0.78 0.55~1.10

P ≤ ①

S ≤ ①

Si Heat analyse 0.40~0.80 0.15~0.35 0.10~0.40 0.15~0.35

Product analyse 0.34~0.86 0.13~0.37 0.08~0.45 0.13~0.37

Ni Heat analyse - - - 0.70~1.00 - 1.20~1.50

Product analyse - - - 0.67~1.03 - 1.15~1.55

Cr Heat analyse 0.50~0.80 0.40~0.65 1.40~2.00 0.40~0.65 - 0.85~1.20

Product analyse 0.46~0.84 0.36~0.69 1.34~2.06 0.36~0.69 - 0.79~1.26

Mo Heat analyse 0.18~0.28 0.15~0.25 0.50~0.65 0.45~0.60

Product analyse 0.15~0.31 0.12~0.28 0.46~0.69 0.41~0.64

B ≤0.0025 0.0005~0.005 0.001~0.005 0.0005~0.006

V Heat analyse - 0.03~0.08 ② 0.03~0.08 - -

Product analyse - -

Ti Heat analyse - 0.01~0.03 0.01~0.10 - - -

Product analyse - 0.01~0.04 0.005~0.11 - - -

Zr 0.05~0.15③ -

0.04~0.16 -

Cu Heat analyse - - - 0.15~0.50 - -

Product analyse - - - 0.12~0.53 - -

Nb Heat analyse - -

Product analyse - -

Note : ① Be suitable for both heat analyse and product analyse.

② Can replace some or all of the Ti composition by 1: 1

③ Zr can be replace by Ce.

When Ce is used, according to heat analyse, Ce/S should be 1.5~1.0

Contact us

1 - Sales department: jw@steel-jw.

com

Skype: join.

win

MSN: join.

win@hotmail.

com

Gmail/G-talk: steel.

join.

win@gmail.

com

Yahoo: steel.

join.

win@yahoo.

com

2 - Warehousing department: warehousing@steel-jw.

com

3 - Marketing department: marketing@steel-jw.

com


4 - Technical department: technical@steel-jw.

com


5 - Financial department : financial@steel-jw.

com

Company Contact:

• Posted By: JOIN-WIN IM/EX

• Phone: 8637165777179

• Address: Chenxu Road,No.10,Jinshui District , zheng zhou , China

• Email:

• Business Description: involved in international trade import export of goods, products, and services