Basecoat Powder Coating - China

Product Description

MT-A2204 basecoat comes in an array of metallic finishes, which offer enhanced exterior durability with the application of a super-durable polyester clearcoat.

These advanced systems incorporate proprietary technology to protect and extend the life of these metallics.

These MT-A2204 basecoat powders are moisture and stain resistant, chemical and chip resistant durable, and built to last in the most challenging environments.

Powder Properties

Chemical Type Polyester

Area of usage Automotive trim parts, roof rail systems

Particle Size Distributon Custom manufactured

Appearance Smooth, satin

Colour Silver metallic

Density (g/cm3) 1.17 ± 0.05

Stoving schedule 10 minutes at 200°C (time at object temperature)

Application Electrostatic

Storage Stability under dry, cool (<25°C) conditions, at least 24 months from production date

Test Conditions

The results are based on mechanical and chemical tests which (unless otherwise indicated) have been carried out under laboratory conditions and are given for guidance only.

Actual product performance will depend upon the circumstances under which the product is used.

Substrate Steel panels, Aluminium

Pretreatment Bonder (WH/60/OC) iron phosphate, Bonder (722/W/OF)

Film thickness 70 µm

Cure schedule 10 minutes 200°C

Pre-treatment

Steel surfaces to be coated must be clean and free from grease.

For maximum protection it is essential to pre-treat components prior to the application of MT-A2204 basecoat.

Iron Phosphate and Zinc Phosphate of ferrous metals improve corrosion resistance.

Aluminium parts require a chromate conversion pre-treatment.

Application

MT-A2204 basecoat powders can be applied by manual or automatic electrostatic spray equipment.

Tribo application is not recommended.

It is recommended that for consistent application and appearance product be fluidized during application.

MT-MW188I must be fully cured otherwise there may be a loss of metallic effect or discoloration of the clear topcoat.

MT-MW188I is not stabilized for direct gas fired ovens.

• All coated pieces should be handled with clean lint free gloves.

• Parts should not be stored in an environment with high humidity.

• Clear coat should be applied as soon as possible after metallic application (maximum time between coats is 8 hours) • Parts should not be passed through a pre-treatment process prior to application of the clear coat Despite the fact that MT-MW188I is a bonded metallic it is not recommended to recycle the powder.

Company Contact:

• Posted By: Standard International Group (HK) Limited

• Phone: +86-21-64208466-808

• Address: Floor 2, #47 Building, 280 Jiugan Road, Songjiang district, Shanghai, China, Shanghai , Shanghai , China

• Email:

• Website: https://moutainchem.com/

• Business Description: Standard International Group (HK) Limited was founded in 2003 - Over years, Standard Group has established long-term strategic cooperative relations with many well-known industrial chemical manufacturers, such as Sherwin-Williams, LANXESS, Evonik, Covestro, Elementis and so on, thus ensuring that customers can receive consistent high-quality services.
  
  Years of professional accumulation make us not only provide high-quality industrial coating additives, but also medicine Pharmaceutical Intermediates and electronic chemistry.
  
  From the painting plant laboratory first sample testing, middle-testing and final-testing, we adhere to the professional, sincere, enthusiastic and efficient service concept, our technical team always adjust the sample during different testing process until it performs perfect chemical reaction at customer’s paints.